Loctite SI 598 BK - 300 ml (oil-resistant silicone)

Loctite SI 598 BK - 300 ml (oil-resistant silicone) (IDH.2061029)

przykład użycia
Product description:
LOCTITE SI 598 cures on exposure to moisture in the air to form a tough, flexible, silicone rubber gasket. This productresists aging, weathering and thermal cycling without hardening, shrinking or cracking. Typical applications include oil pans, transmission pans, valve covers, valves and guides, timing gear covers, and differential covers. This product is typically used in applications with an operating range of -54 °C to 260 °C. Further information on the product can be obtained from your local technical department: biuro@woronko-loctite.pl

Steps to achieve the best adhesive results:
1. For best performance bond surfaces should be clean and free from grease. Use LOCTITE SF 7063.
2. Full performance properties will develop over 72 hours.
3. Moisture curing begins immediately after the product is exposed to the atmosphere, therefore parts to be assembled should be mated within a few minutes after the product is dispensed.
4. Excess material can be easily wiped away with non-polar solvents. NOTE: LOCTITE SI 598 is not recommended for use as a cylinder head gasket or head gasket sealant.
5. For full automatic applications a volumetric dispensing system is recommended.

Storage:
Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.
Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties.
Material removed from containers may be contaminated during use. Do not return product to the original container.
Henkel Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated.

Parameters:
  • Time to full cured at the gap 0,5 mm (23 °C) : 4 days
  • Shear strength:
    -Aluminum : 0,2 N/mm²
    -Zinc dichromate : 0,5 N/mm²
    -Shot blasted steel : 1,2 N/mm²
    -Honed aluminum : 0,5 N/mm²
  • Tensile strength : 1,6 N/mm²
  • Working temperature : from -55 °C to +200 °C
  • Hardness : 32 Shore A
  • Color : black
  • Elongation at break : 340%


Full technical information can be found in the technical data sheet.